|Year : 2019 | Volume
| Issue : 2 | Page : 36-40
Bulk-fill versus conventional composite: A comparative analysis on degree of conversion
Fernanda Ferreira de Albuquerque Jasse1, Hélida Gomes de Oliveira Barud1, Juliana Maria Capelozza Boaventura1, Cristiane de Melo Alencar1, Alexandre Gatti2, Edson Alves de Campos1
1 Department of Restorative Dentistry, Araraquara School of Dentistry, Araraquara, Brazil
2 Araraquara Chemistry Institute, University of São Paulo – UNESP, Araraquara, Brazil
|Date of Web Publication||8-Jul-2019|
Prof. Fernanda Ferreira de Albuquerque Jasse
Rua Humaitá, 2019, Apartament 11, Center Zip Code 14804-300, Araraquara, São Paulo
Source of Support: None, Conflict of Interest: None
Aim: This study aimed to determine the degree of conversion (DC) of two resin-based composites: a conventional nanohybrid composite and a bulk-fill flowable composite (SureFil® SDR™ flow). Materials and Methods: DC was evaluated at 1-, 2-, 3-, and 4-mm depths at varying irradiation times (20 and 40 s) by Fourier-transform infrared spectroscopy. Disc-shaped specimens of varying depths were prepared and photoactivated with a third-generation light-emitting diode light-curing unit. The specimens were stored for 24 h in the dark at ambient temperature and pulverized into a fine powder which was mixed with potassium bromide. After homogenization, the mixture pressed to form a pellet. All pellets were evaluated by an infrared spectrometer equipped with a triglycine sulfate detector using diffuse reflectance. The percentage of monomer conversion was determined from the ratio of the absorbance intensities of the aliphatic carbon–carbon double bonds (C = C) and the internal standard before and after the curing of the composite, represented by the aromatic carbon–carbon single bonds (C-C). Results: The DC data for the bulk-fill resin showed no significant difference (P > 0.05) for different irradiation depths, whereas for the conventional nanohybrid resins, statistical analyses revealed a significant result of the variables time and depth as well as the interaction between them. Conclusions: The results indicated that SDR™ achieves a 4-mm depth of cure with both 20- and 40-s light exposures.
Keywords: Bulk-fill flowable, composite resins, degree of conversion
|How to cite this article:|
Jasse FF, Barud HG, Boaventura JM, Alencar Cd, Gatti A, Campos EA. Bulk-fill versus conventional composite: A comparative analysis on degree of conversion. Eur J Gen Dent 2019;8:36-40
|How to cite this URL:|
Jasse FF, Barud HG, Boaventura JM, Alencar Cd, Gatti A, Campos EA. Bulk-fill versus conventional composite: A comparative analysis on degree of conversion. Eur J Gen Dent [serial online] 2019 [cited 2019 Oct 21];8:36-40. Available from: http://www.ejgd.org/text.asp?2019/8/2/36/262215
| Introduction|| |
Since the introduction of composites in the early 1960s, resin-based materials have shown a constant technical progress with regard to new types of filler particles. However, despite the evolution of resin-based materials, conventional composite resins used at the beginning of the 21st century still present unfavorable aspects such as an insufficient degree of monomer conversion  and generation of stress by polymerization shrinkage upon curing.
No material can be “ideal:” exhibiting a high degree of conversion (DC) and minimal polymerization shrinkage. These features vary generally antagonistically because a high DC occurs when the chemical interlacing of the monomers is increased, which consequently produces a higher volume shrinkage. The main problem of a higher volume shrinkage is the higher concentration of stress induced on the cavity walls, which may result in cracks, gaps, secondary caries, and postoperative sensitivity. In turn, a lower DC may create problems such as release of unreacted monomers  or high water sorption.
Manufacturers have claimed that bulk-fill resins reach a satisfactory DC, leading to a maximal increment thickness of 4–5 mm, depending on the trademark, which can dispose of the need for applying and curing composite resins in increments of limited thickness. The bulk-filling of cavities, besides saving clinical time, also prevents the formation of air bubbles and contamination between these increments, thus favoring the homogeneity of the restorative material. Therefore, bulk-fill resins have been increasingly studied.
It is well known that light energy transmission through a composite is attenuated drastically with increasing depths from the light-irradiated surface. Therefore, increments of conventional composite resins are limited to 2 mm. A decrease in monomer conversion can compromise physical properties and clinical performance of the restorations  because DC is a codetermining factor of the physical and chemical properties of restorative resins, such as hardness, wear resistance, compressive strength, flexural strength, dimensional stability, solubility, discoloration, and degradation reactions. Studies have found that the release of unreacted monomers that remain in the material  may stimulate bacterial growth around the restoration, irritate soft tissues, and cause allergic reactions in some patients.,
Several methods have been used to assess the DC: infrared spectroscopy, calorimetry, Raman scattering, and even indirect techniques such as measuring hardness in the top and bottom. Both infrared spectroscopy and Raman spectroscopy are classified as vibrational techniques because they are sensitive to the vibrational modes of molecules, whereas calorimetry allows measurement of the methacrylate group conversion through an exothermic polymerization reaction. Among the spectroscopic techniques commonly reported in the literature, Raman technique has the advantage of analyzing the material without any sample preparation; however, Fourier-transform infrared (FTIR) technique has traditionally provided more useful information on the monomer conversion of dental composites.
Although several techniques have been described in the literature to assess DC, the development of bulk-fill resins brings with it the need to adapt the existing techniques. This is especially true for the preparation of specimens as manufacturers advertise that the specimens are adequately photoactivated in increments up to 4 mm in depth. This specification is not in accordance with the International Organization for Standardization (ISO) 4049 standard for testing composites.
Therefore, the aim of this study was to evaluate the DC of a bulk-fill flow composite through FTIR analysis in comparison to a nanohybrid composite resin containing a conventional matrix at different specimen depths and irradiation times. The following null hypotheses were tested: (1) depth has no significant influence on DC, (2) irradiation time has no significant influence on DC, and (3) the bulk-fill flow composite shows no difference in DC behavior when compared with the conventional material.
| Materials and Methods|| |
[Table 1] shows the resin composites tested.
|Table 1: Summary of the dental resin composites investigated in this study|
Click here to view
To determine DC at different depths, a set of four cylindrical molds was prepared according to the schematic shown in [Figure 1]. The molds (1-mm depth and 4-mm diameter) were successively filled and superposed on each other, with a polyester strip separating consecutive molds. The light-emitting diode light-curing unit (LED LCU) (Bluephase G2, Ivoclar Vivadent, Schaan, Liechtenstein, Europe) tip was then placed on the upper surface of the set of molds through a glass slide, and light was activated in the high-power mode (approximately 1100 mW/cm 2) for either 20 or 40 s. Then, the specimens were carefully removed from the molds and identified according to the number of the samples and its depth (i. e., 1, 2, 3, and 4 mm). Five replicates (n = 5) were performed for each composite resin. The specimens were then stored for 24 h in the dark at 37 ± 1°C before analysis.
Degree of conversion (%) analysis
After storage, the composites were pulverized into a fine powder which was weighed (5 mg) and thoroughly mixed with powdered potassium bromide salt (100 mg). The obtained mixture was inserted into a pelleting device and pressed with a load of 10 t for 1 min to obtain a pellet.
The pellets were analyzed using a FTIR spectrophotometer (Nexus-470 FT-IR, Thermo Nicolet, EUA) to measure the DC of the composites. DC is defined by the number of carbon–carbon double bonds (C = C) that are converted into carbon–carbon single bonds. FTIR spectra of both uncured and cured samples were obtained through a triglycine sulfate (TGS) detector using diffuse reflectance coupled to a computer. The spectra were recorded in the absorbance mode with the following predetermined settings: 32 scans, 4 cm −1 resolution, and 300–4000 cm −1 wavenumber.
Following Ribeiro et al., the percentage of unreacted carbon double bonds (% C = C) is obtained as the ratio between the absorbance intensities of the aliphatic C = C (peak at 1638 cm −1) and the internal standard before and after composite curing, represented by the aromatic C–C (peak at 1608 cm −1). DC was determined according to the following formula:
Statistical analysis was performed for the evaluation of data normality (Shapiro–Wilk test) using SPSS software version 13.0 (SPSS Inc., Tulsa, OK, USA). The assessment of DC was carried out by two-way analysis of variance (ANOVA). Multiple comparisons of DC means by Bonferroni test followed the analysis. All statistical analyses were performed at 5% significance level.
| Results|| |
Results are listed in [Table 2]. Two-way ANOVA of the DC data for the SDR™ resin showed no significant difference (P > 0.05) for the various irradiation depths. The mean DC of SDR™ varied from a maximum of 78.24 (±3.46)% at an irradiation depth of 2 mm (irradiated for 40 s) to a minimum of 73.20 (±2.92)% at an irradiation depth of 4 mm (irradiated for 20 s). For Esthet-X™, two-way ANOVA and Bonferroni test revealed a significant effect of the variables time and depth as well as the interaction between them. DC varied from a maximum of 74.79 (±2.63)% (2 mm, irradiated for 40 s) to a minimum of 3.94 (±9.50)% (4 mm, irradiated for 20 s).
|Table 2: Mean and standard deviation of degree of conversion evaluated on specimens of variable depths after different irradiation times|
Click here to view
Considering DC as a function of irradiation time, a difference could be observed only for Esthet-X™ at 4-mm depth, where 40 s of irradiation exhibited a significantly better DC than 20 s of irradiation. However, for Esthet-X™, the DCs of 1 mm and 2 mm (for both 20 and 40 s of irradiations) are statistically similar, decreased linearly for 3 mm and 4 mm. SDR™ exhibited no differences between irradiation times for all depths. Both composite resins performed similarly for depths of 1 mm and 2 mm.
| Discussion|| |
It is well known that light energy emitted from an LCU decreases when transmitted through composites. Hence, more the distance from the irradiated surface, the lower will be the DC of the resin-based material. Therefore, we considered incremental techniques to apply and cure resin composites with increments of 2-mm maximal thickness., However, in contrast to these principles, the use of bulk-fill composites with increments of 4-mm maximal thickness is advocated nowadays, allowing a less time-consuming and safer restoration technique than before, especially for deep cavities. The results of this study show that 4-mm SDR™ samples photoactivated for 20 s meet the manufacturer's expectations. Thus, a molar with a Class II mesio-occlusal-distal cavity of about 6-mm deep in proximal boxes restored with a bulk-fill resin can save less than half the clinical time it would take when restored by the conventional incremental technique. This is possible because a single increment of 4 mm can fill the two proximal boxes and part of the occlusal box and polymerize it in just 20 s and the other 2 mm if left can be filled in three conventional increments (increments of no more than 2 mm with a conventional resin) polymerized for at least 20 s each. Thus, it adds to 80 s of photoactivation, whereas for conventional techniques, this would need approximately 10 increments using a conventional resin for filling the same cavity, each being cured for at least 20 s, totaling 200 s in all.
More than 25 years ago, the ISO introduced a method for defining the depth of cure of resin composites, the well-known “ISO 4049; Depth of cure.” According to this method, tube-shaped specimens of the tested resin are light-cured, and the uncured part of the resin is then scraped away. The depth of cure is then given by the total length of the residual hard tube divided by the factor 2. The resulting value determines the maximum increment thickness of the tested resin. Because resin composites are in continuous development with regard to their composition and properties, studies have tested new ways to evaluate the depth of cure of new resins, especially for bulk-fill ones.,, In a study published in 2012, the authors verified the accuracy of the ISO 4049 method when used for bulk-fill materials and concluded that the method overestimates the depth of cure. Based on these findings, an alternative method was used in this study to determine the depth of cure through the DC assessment of each millimeter of resin samples.
Many studies have assessed the DC of the external surface of a restoration using simple techniques; however, the evaluation of monomer conversion in the inner layers of resins is not simple to assess. In the current study, a matrix has been synthesized specifically for the assessment of the DC of the resins at different depths. A similar device was used by Finan et al., who assessed the DC in specimens that are up to 8-mm deep and 11-mm diameter. In the previously mentioned study, the authors observed a maximum DC of 59% for SDR™ at an irradiation depth of 1 mm and at least 45% at a depth of 8 mm. In the present study, using a similar methodology, SDR™ resin achieved a maximum DC of 76% considering the same irradiation time of 20 s. The difference between these results can probably be due to the photoactivation unit. We used a high-intensity LED, whereas the other study used a quartz-tungsten-halogen LCU (operated at an output intensity of 650 ± 26 mW/cm 2). Rueggeberg et al. also reported the variation when the infrared spectroscopy technique was used, more specifically to the standard baseline technique that was used when C = C peak intensities are determined. They pointed out that baselines can be drawn in a number of locations, and not all researchers draw baselines in a similar manner. Thus, results for DC may be imprecise when interlaboratory results are compared.
The evaluation of DC permits characterization of the conversion of monomers into polymers. Several methodologies can be used to assess the DC of composite resins. FTIR spectroscopy is a technique that may be applied for the evaluation of the conversion of monomers into polymers by calculating the ratio of the aliphatic C = C absorption at 1638 cm −1 to the aromatic C = C absorption at 1608 cm −1. This technique is well reported in the literature; however, recent studies ,,, have used infrared spectroscopy with attenuated total reflection (ATR) because of its simplified sample preparation when compared to the TGS detector. Considering the technique used in this study, Shin et al. highlighted the fact that preparing samples as thin and fragile sections is one of the disadvantages of the technique. However, we consider that by crushing the specimens, we are using a portion of the specimen's constituent for analysis and not just its surface of it, as it happens when the ATR crystal is used.
The efficiency of polymerization is completely dependent on the characteristics of the light produced. Thus, a third-generation LED LCU was chosen because its peak emission coincides with the maximum absorption of the camphorquinone, which is the photoinitiator present in both tested resins  to achieve best results for the tested materials, without any adverse influence of LCU on the results. In addition, two different curing times were used (20 and 40 s). Although manufacturer's recommendation indicates only 20 s, this study evaluated a longer time aiming to verify any potentiating effect on DC.
In this in vitro study, depth influences the DC of the Esthet-X™ resin but not SDR™. Therefore, the first null hypothesis was partially accepted. The same is true for the second null hypothesis because the irradiation time influenced only the Esthet-X™ resin. However, up to a depth of 2 mm (the maximum increment recommended by the manufacturer), irradiation time did not have any influence because, for both times tested, the DC values were statistically similar. The third null hypothesis was rejected because the materials tested behaved differently with regard to the DC.
This study evaluated only one bulk-fill material, which is a limitation to generalizing the conclusions. More studies need to be carried out to assess the behavior of other brands of bulk-fill composites.
| Conclusions|| |
- This study indicates that SDR™ achieves a 4-mm depth of cure with both 20- and 40-s light exposures
- Depth has a significant influence on the DC of Esthet-X™ but not of SDR™
- Irradiation time does not have any significant influence on the DC of SDR™, while it influences that of Esthet-X™.
Financial support and sponsorship
This study was financially supported by the Coordination of Improvement of Higher Education Personnel of the Brazilian Government.
Conflicts of interest
There are no conflicts of interest.
| References|| |
Mitra SB, Wu D, Holmes BN. An application of nanotechnology in advanced dental materials. J Am Dent Assoc 2003;134:1382-90.
Sakaguchi RL, Douglas WH, Peters MC. Curing light performance and polymerization of composite restorative materials. J Dent 1992;20:183-8.
Davidson CL, Feilzer AJ. Polymerization shrinkage and polymerization shrinkage stress in polymer-based restoratives. J Dent 1997;25:435-40.
Dewaele M, Truffier-Boutry D, Devaux J, Leloup G. Volume contraction in photocured dental resins: The shrinkage-conversion relationship revisited. Dent Mater 2006;22:359-65.
Amirouche-Korichi A, Mouzali M, Watts DC. Effects of monomer ratios and highly radiopaque fillers on degree of conversion and shrinkage-strain of dental resin composites. Dent Mater 2009;25:1411-8.
Ferracane JL, Mitchem JC. Relationship between composite contraction stress and leakage in class V cavities. Am J Dent 2003;16:239-43.
Ilie N, Obermaier J, Durner J. Effect of modulated irradiation time on the degree of conversion and the amount of elutable substances from nano-hybrid resin-based composites. Clin Oral Investig 2014;18:97-106.
Kruly PC, Giannini M, Pascotto RC, Tokubo LM, Suga US, Marques AC, et al.
Meta-analysis of the clinical behavior of posterior direct resin restorations: Low polymerization shrinkage resin in comparison to methacrylate composite resin. PLoS One 2018;13:e0191942.
Łagocka R, Mazurek-Mochol M, Jakubowska K, Bendyk-Szeffer M, Chlubek D, Buczkowska-Radlińska J. Analysis of base monomer elution from 3 flowable bulk-fill composite resins using high performance liquid chromatography (HPLC). Med Sci Monit 2018;24:4679-90.
Sideridou I, Achilias DS, Spyroudi C, Karabela M. Water sorption characteristics of light-cured dental resins and composites based on bis-EMA/PCDMA. Biomaterials 2004;25:367-76.
Chung KH, Greener EH. Correlation between degree of conversion, filler concentration and mechanical properties of posterior composite resins. J Oral Rehabil 1990;17:487-94.
Moore BK, Platt JA, Borges G, Chu TM, Katsilieri I. Depth of cure of dental resin composites: ISO 4049 depth and microhardness of types of materials and shades. Oper Dent 2008;33:408-12.
Leprince JG, Leveque P, Nysten B, Gallez B, Devaux J, Leloup G, et al.
New insight into the “depth of cure” of dimethacrylate-based dental composites. Dent Mater 2012;28:512-20.
Shin WS, Li XF, Schwartz B, Wunder SL, Baran GR. Determination of the degree of cure of dental resins using Raman and FT-Raman spectroscopy. Dent Mater 1993;9:317-24.
Silva EH, Albuquerque RC, Lanza LD, Vieira GC, Peixoto RT, Alvim HH, et al.
Influence of different light sources on the conversion of composite resins. Indian J Dent Res 2011;22:790-4. [Full text]
Finan L, Palin WM, Moskwa N, McGinley EL, Fleming GJ. The influence of irradiation potential on the degree of conversion and mechanical properties of two bulk-fill flowable RBC base materials. Dent Mater 2013;29:906-12.
Ribeiro BC, Boaventura JM, Brito-Gonçalves JD, Rastelli AN, Bagnato VS, Saad JR. Degree of conversion of nanofilled and microhybrid composite resins photo-activated by different generations of LEDs. J Appl Oral Sci 2012;20:212-7.
Price RB, Murphy DG, Dérand T. Light energy transmission through cured resin composite and human dentin. Quintessence Int 2000;31:659-67.
Flury S, Hayoz S, Peutzfeldt A, Hüsler J, Lussi A. Depth of cure of resin composites: Is the ISO 4049 method suitable for bulk fill materials? Dent Mater 2012;28:521-8.
International Organization for Standardization. ISO 4049:1988(2). Dentistry-Resin-based Filling Materials. Sant-Denis, France: International Organization for Standardization; 1988.
Czasch P, Ilie N.In vitro
comparison of mechanical properties and degree of cure of bulk fill composites. Clin Oral Investig 2013;17:227-35.
Rueggeberg FA, Hashinger DT, Fairhurst CW. Calibration of FTIR conversion analysis of contemporary dental resin composites. Dent Mater 1990;6:241-9.
Garoushi S, Vallittu P, Shinya A, Lassila L. Influence of increment thickness on light transmission, degree of conversion and micro hardness of bulk fill composites. Odontology 2016;104:291-7.
Uhl A, Sigusch BW, Jandt KD. Second generation LEDs for the polymerization of oral biomaterials. Dent Mater 2004;20:80-7.
[Table 1], [Table 2]